1. Product Feature of Electronic Potting Silicone Rubber
HY-9055 silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of  PC(Poly-carbonate)PPABSPVC, etc. and metal materials.

2. Typical Application of Electronic Potting Silicone Rubber

HY-9055 electronic potting silicone rubber could be applied to

- high powered electronics,  

- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.

-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. 
3. Technical Guidelines of of Electronic Potting Silicone Rubber 

a, Pls put part A and part B in separate container and stir evenly before mixing the two part together.

b, Mixing Ratio: part A: part B = 1:1 

c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.

Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80100℃, the silicone will cure in 15 minutes; while in 25℃ room temperature, the silicone will cure around 8 hours.

4.Notes of Electronic Potting Silicone Rubber
a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas.

Organotin compound or Condensation silicone with organotin

Sulphur, sulfide and sulfur rubber materials.

Amine compounds as well as contains the amine materials.

Pewters solder flux

b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.

c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes.

d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.
Technical Parameters of of Electronic Potting Silicone Rubber

Features

Part A

Part B

Before Curing

Appearence

Gray Fluid

White Fluid

Viscosisty25℃cps

2500±500

2500±500

Operation features

Mixing Ratio

11

Viscosisty(after mixing) cps

20003000

Operating Time25℃  hr

120

Curing time min25℃

480

Curing time80℃  hr

20

 

 

After Curing

HardnessShore  A

55±5

Thermal conductivity [Wm·K]

≥0.8

Dielectric StrengthKV/mm

≥25

Permittivity1.2MHz

3.03.3

Volume ResisivityΩ·cm

≥1.0×1016

linear expansibility [m/m·K]

≤2.2×10-4

Fire Resistance   

94-V1

(Pls note: the above data for this product in 25 ℃ temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers when using.)
PACKAGE
40Kg/pail as a set (Part A 20Kg + Part B 20Kg) 

SHELF LIFE AND TRANSPORTATION

1. Twelve(12) months when stored at 24C in tightly closed original packages.

2. This kind of product is non-dangerous product, which could be transported as general chemicals.

3. Storage beyond the expired date doesnot necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

For more information, please feel free to contact Mr. Timo

Tel: +86-0755-89212365

Mob: +86-18938867564

Skype: Hyjtimo

 

Product Detail Image

electronic potting silicone

electronic potting silicone

electronic potting silicone